This study was performed to test the combustive properties of Medium Density Fibreboards (MDFs) treated with chemicals of the bis-(dimethylaminomethyl) phosphinic acid (DMDAP), N,N-dimethylethylenediaminomethyl-bis-phosphonic acid (DMDEDAP), piperazinomethyl-bis-phosphonic acid (PIPEABP), and methylpiperazinomethyl-bis-phosphonic acid (MPIPEABP). MDFs were painted in three times with 15 wt% solution of the bis-(dimethylaminomethyl) phosphinic acid and alkylenediaminoalkyl-bis-phosphonic acids at the room temperature, respectively. After drying MDF treated with chemicals, combustive properties and volatile organic compounds (VOCs) contents were examined by the cone calorimeter (ISO 5660-1), test for flame retardant (NEMA Notice No. 2012034), and gas chromatography (KS M ISO 11890-2), respectively. It was indicated that the MDFs treated with chemicals showed the longer time to combustion time (CT) = (442~492) s than that of virgin plate by reducing the burning rate except for CT treated with DMDAP. In adition, the MDFs treated with chemicals showed both of the higher char area (44.33~61.33) kg/kg and char length (10.33~11.67) cm than those of virgin plate. Especially, the MDFs treated with chemicals showed the higher mean volatile organic compounds (VOCs) (0.188~0.333) g/L than that of virgin plate within the prescribed limits. Thus, It is supposed that the combustion- retardation properties were improved by the partial due to the treated chemicals in the virgin MDF.