This paper presnets the characteristics of electropolymerization and electrochemicla propoerties of polyaniline(PAn). From the morphology study on the PAn surface, it seems that coagulation of the fibrils on the surface proceeds as the PAn grows, resulting in fibril clusters with new branches and more extensive voids. While PAn/Li cell is cycled at potential range between 2.9V and 3.7V in which the first strong reduction peak of 2.75V does not appear, its oxidation reduction capacities were increased up to about tenth cycle. Electricity efficiency of stable charge-discharge to deep discharge in PAn/Li cell was 42.9%. Average charge potential, avergae discharge potential, energy density, and charge-discharge energy efficiency of the PAn/Li cell were 3.4V, 3.25V, 132.9Wh/kg, and 95.6%, respectively.