The compositions and microstructures of Pb-Sn alloy electrodeposits were investigated in terms of the electrolysis conditions conditions by using fluoborate bath. The Pb content of alloy deposit decreased with increasing dreasing current density until the limting content was obtained. The proferred orientation of Pb-phase in the alloy changed in the sequence of (110)longrightarrow(100)longrightarrow(100)+(110)(311)longrightarrowrandom distribution of crystals with increasing cathode overpotential, while that of $eta$-Sn phase was (110)(301)(211)n mixed texture. The smooth surface with granular crystallites was obtained below medium current desity, while the rough surface texture was formed at high current density.