The surface modification of a mild and stainless steel by alumina sprayed coating were studied. The effects of surface roughness and bond coating layer on the adhesive strengthy and durability of sprayed specimens were also investiated. The adhesive strength of ceramic coating was affected by surface roughness and bond coating layer thinkness. That showed excellent undergrit blast time and bond coating layer; 60 sec and 0.15-0.33mm, respectively. The adhesive strength and densification of sprayed coating with air pressure were superior to those of without and fracture was mainly occured at alumina-bond coating interface. Under ambient atmosphere at $800^{circ}C$, the oxides existed within bond coating layer promote diffusion of oxygen to lower durability of sprayed specimens. In this case, fracure was occured at sudstrate-bond coating interface.