Effects of MnO2 addition ranged from 0.0wt% to 5.0wt% on the microstructure and dielectric and piezoelectric properties of the Pb(Zr0.52 Ti0.48)O3 Ceramics have been investigated. The solubility limit of MnO2 in Pb(Zr0.52 Ti0.48)O3 is about 0.5wt%, and MnO2 as a valence state of Mn3+ is substituted for (Zr, Ti) lattice site in PZT solid-solution. The addition of MnO2 up to 0.5wt% in Pb(Zr0.52 Ti0.48)O3 brings increase of density, but decreased of grain size and tetragonality. Dielectric constant slightly decreases, but both coupling factor(Kp) and mechanical quality factor(Qm) increase with the addition of MnO2. However, excess amount of MnO2 addition more than 0.75wt% results in rapid decrease of resistance. Dielectric constant and tan $delta$ increase due to the second phase and inhomogeneous Mn distribution.