Silicon carbide has been grown by a chemical vapor deposition (CVD) technique using CH3SiCl3 and H2 gaseous mixture onto a graphite substrate. Based on the thermodynamic equilibrium studies and the suggestion that the deposition rate of SiC is controlled by surface reaction theoretical kinetic equation for CVD of silicon carbide has been proposed. The proposed theoretical kinetic equation for CVD of silicon carbide agreed well with the experimental results for the variation of the deposition rate as a function of the partial pressure of reactant gases. The Vikers microhardness of the SiC layer was about 3000∼3400 kg/$ extrm{mm}^2$ at room temperature.