Recrystallization behaviors of ordered and disordered structures in $Ll_2$ type $Ni_3Fe$ alloy were studied through hardness measurement and differential thermal analysis. When the disordered structure was isothermally aged at $480^{circ}C$ below order-disorder transition temperature, the hardness of the structure was increased due to progressive ordering with increasing aging time. The hardness of the disordered structure was increased rapidly with increasing deformation degree up to 10%, and then gradually increased with further deformation degree. while the hardness of the ordered structure was increased rapidly with increasing deformation degree up to 10%, showing a constant hardness value up to 50% and gradually decreased with further deformation degree. The hardness of the ordered structure was higher than that of the disordered structure at all same deformation degrees. The recrystallization temperature of the ordered and disordered structures were decreased with increasing deformation degree. At the same deformation degrees, the recrystallization temperature of the ordered structure was lower than that of the desordered structure.