Growth runs of KTP single crystals were carried out by the hydrothermal method. KTP powders used for the crystal growth were prepared as a single phase by the solid state reaction of a stoichiometric mixture of $KH_2PO_4 and TiO_2$ at TEX>$800^{circ}C$</TEX> and subsequently by the hydrothermal treatment at $250^{circ}C$ 4m KF solution. The most effective solvents for the crystal growth of KTP were KF and K $K_2HPO_4$ solutions. Solubilities of KTP in these solutions were positive over the range $350~450^{circ}C$.Seed crystals of good quality could be obtained by the horizontal temperature gradient method at temperatures over the range 380~430^{circ}C$ in these solutions. The hydrothermal conditions for the high growth rates of seed crystals are as follows: growth method; vertical temperature gradient method, solvent; 4m KF or $K_2HPO_4$ solution, temperature region; $400~450^{circ}C$, pressure region; $1000~1500kg/cm^2$, where solubility of KTP was large enough to proceed the growth. Under such conditions, seed crystals of KTP are grown at a rate of approximately 0.06-0.08mm/day in the direction of the c-axis. Morphologies of grown crystals tended to be bounded by (100), (011) and (201) faces.