Effects of $Ta_2O_5,ZrO_2$ and $SiO_2$ addition on magnetic properties of 0.02wt%$Bi_2O_3$ and 0 . 0 5 wt%$CaCO_3$ doped Mn-Zn ferrites(58.5mol% $Fe_2O_3$, 25.5 mol% ZnO) were investigated. E:lectrlcal resistivity and magnetic properties such as the initial permeability($mu_i$), loss factor(tan$delta$), coercive force Hc(m0c) were measured. With lncreasing $Ta_2O_5$ and $ZrO_2$ addition, the following effects were observed: I ) Decreasing of the average grain size; 2) lncreasing of the electrical resistivity and initial permeability; 3) Ilecreasmg of loss factor values. (very low loss esprcially at high frequency region) ; 4 ) Fine and uniform microsrructures were obtamed at O.lwt% nddecl samples. In case of $SiO_2$ addition, anomalous grain growth and degradation of magnetic properties were observed. The obtained maximum initial permeability value was 6260 at IOkHz. $25^{circ}C$ from 0.02wt%$Bi_2O_3$. 0.05wt%$CaCO_3$, 0.lwt%$Ta_2O_5$ added sample, the corresponded relative loss factor (tan$delta /mu_i$)for the sample was $4.2 imes 10^{-6}$.