Structural and optical characteristics in $SnO_2$/a-Se/Al sample by aging variation and applying constant voltage had been investigated. a-Se was varied with monoclinic structure and its surface was greatly exchanged. Its capacitance was first decreased and then increased and its photo-current, photo-voltage and photo-capacitance were increased gradually with day and applying voltage. From the results, crystallization of a-Se and dopant trap level formation had been identified. Also, it was acknowledged $SnO_2$/a-Se/Al sample is useful in photovoltaic and solid thin film cell.