Properties of oxynitride films reoxidized by $N_2{O}$ gas after thermal oxidation and $N_2{O}$ oxide films directly oxidized by using $N_2{O}$ gas on the bare silicon wafer have been studied. From the AES analysis, nitrogen pile-up at the interface of Si/oxynitride and Si/$N_2{O}$ oxide has observed. $N_2{O}$ oxide and oxynitride films have the self-limited characteristics. Therefore, it will be possible to obtain ultra-thin films. Nitrogen pile-up at the interfaces of Si/oxynitride and Si/$N_2{O}$ oxide strengthens film structure and improves dielectric reliability. Although fixed charge densities and interface trap densities of N20 oxide and oxynitride films have somewhat higher than those of thermal $SiO_2{O}$, $N_2{O}$ oxide and oxynitride films showed improved I-V characteristics and constant current stress.