In this study, the TSC spectroscopy has been applied to investigate the influence of structural change due to a process of curing reaction on the electrical properties of epoxy composites cured with acid-anhydride. Five TSC peaks appeared in -160-250[.deg.C]: in the low temperature region below glass transition temperature(T$\_$g/), three relaxation mode peaks due to action of side chains, substitution group or terminal groups have been observed, a peak associated with T$\_$g/, appeared in 110[.deg. C] and p peak due to ionic space charges located in 150[.deg.C]. Each peak was separated into elementary peaks by the partial polarization procedure, and the distribution of activation energy and relaxation time were analized to clearify the origin of each peak. Also, overaboundantly added hardener separated a .betha. peak near 10[.deg. C] into two peaks of .betha.$\_$1/(10.deg. C) and .betha.$\_$2/(20.deg. C) according to increasement of forming field, and the separated hardener was oxidated thermally with increasing surrounding temperatures. The expansion of the free volume need in molecular motion and the reduction of the structural packing density through thermal oxidation process increased TSC between .alpha. peak and .betha. peak and decreased T$\_$g/.