In this study, ln$_{1-x}$ Ga$_{x}$P alloy crystal which has different compositions were grown by the temperature gradient solution(TGS) method, and the properties of deep levels were measured in the temperature range of 9OK-450K. We find the four deep levels of E$_{1}$, E$_{2}$(248meV), E$_{3}$(386meV) and E$_{4}$(618meV) in GaP, which has composition of Ga in In$_{1-x}$ Ga$_{x}$P is one, and the trap densities of E$_{3}$ and E4 levels were 7.5*10$^{14}$ cm$^{-3}$ and 9*10$^{14}$ cm$^{-3}$ , respectively. A broad deep level spectra was revealed in In$_{1-x}$ Ga$_{x}$P whose composition of Ga, x, were 0.56 and 0.83, and the activation energy and trap densities were about 430meV and 6*10$^{14}$ cm$^{-3}$ , respectively.ectively.