A double layered photoreceptor using phthalocyanine dye was made by dip-coating method. The under cutting layer(UCL) was coated with A1$\_$2/O$\_$3/ or polyamide, and the charge generation layer(CGL) was formed by .tau.-type metal-free phthalocyanine. The oxadiazole was used as a charge transport layer(CTL) and polycarbonate and poly(vinyl butyral) was employed as a host polymer. The .tau.-H$\_$2/Pc had an absorption peak around 780nm, which coincided with the emitting wavelengths of GaAlAs diode lasers. Maximum charge acceptance of CTL that gives thickness of 12.mu.m was -900V by corona charge of -6.0kV. In photo-induced discharge measurements, residual potential was less than -20V and sufficient for ordinary use, and sample films using of poly(vinyl butyral) was showed good charge retention. In printing test, drum that was employed polycarbonate as a host polymer showed the good print quality.