Dielectric and structural properties of $Ba_{1-x}$(Z $n_{1}$3/T $a_{2}$3/) $O_{3}$+1 mol% Mn $O_{2}$ (x=0, 0.01, 0.02, 0.03, 0.04) ceramics was investigated at microwave frequencies. With $Ba_{+2}$ shortage, the sinterability and the unloaded Q( $Q_{u}$) were much improved, and the ordering in B site and the lattice distortion was greatly enhanced and the structure approached the completely ordered structure. $Q_{u}$ was strongly correlated with these factors such as ordering ratio, lattice distortion and sinterability, and had the maximum value of 7500 at x=0.01. The dielectric constant was near 30 and the temperature coefficient of the resonant frequency was 2 ppm/.deg. C at x=0.01.1.1.1.