Frequency-dependent electrical properties of $C_{22}$-Quinolinium(TCNQ) LB films were investigated in a frequency range of 10[Hz]-13[MHz] along a perpendicular direction. The films were heat-treated to understand an electrodynamic response in a temperature range of 20-240[.deg. C]. Frequencydependent dielectric constants show that there are two characteristic dispersions; one is a dispersion occuring near 1[MHz] coming from the orientational polarization of the molecules and the other one is an interfacial polarization effect below 1[kHz] or so when the annealing temperature is above 80 [.deg. C]. The overall frequency-dependent dielectric constant is higher near 80[.deg. C]. It may be due to a softness of the alkyl chains. Several other methods were employed to identify the internal structure change of the films. DSC(differential scanning calorimetry) data of the $C_{22}$-Quinolinium(TCNQ) molecules shows that there is an endothermic process near 110[.deg. C] and a weak exothermic process near 180[.deg. C]. While the endothermic process is related to a disordering of the alkyl chains, the exothermic process seems to be due to a chemical structure change of the TCNQ molecules. Thickness measurement by ellipsometry shows that there is a thickness drop near 100[.deg. C], and the thickness above 120[.deg. C] becomes around 20[%] of the room-temperature value.lue.