Solid solutions Sr$_{2}$(Ta$_{1-x}$ Nb$_{x}$)$_{2}$O$_{7}$, (x=0.0-1.0), composed of strontium tantalate(Tc=-107.deg. C) and strontium-niobate(Tc=1342.deg. C) were prepared by the conventional mixed oxide method and the flux method(molten salt synthesis method). Phase relation, sintering temperature, grain-orientation and dielectric properties for sintered ceramic samples were investigated with different compositions. Both Curie temperature and dielectric constant at Curie temperature were increased, and sintering behavior and the degree of grain-orientation were improved with the increase of Nb content. The single phase Sr$_{2}$(Ta/sib 1-x/Nb$_{x}$)$_{2}$O$_{7}$ powder was synthesized by using the flux method at lower temperatures, and sintering temperature was also reduced by using the flux method-derived powder than using the mixed oxide-derived powder. Sintering characteristics and dielectric properties of the specimens prepared by the flux method were better than those derived through the conventional mixed oxide method.thod.hod.