Thin fihn SnO$_{2}$ Gas Sensor was fabricated by electron-beam evaporation system and the target made by general firing method for the purpose of detecting gas components in air, especially methane gas. SnO$_{2}$ thin film was prepared on the polished alumina substrate which Pt interdigital electrode was precoated. The effects of annealing temperature and substrate temperature on the structural properties of SnO$_{2}$ thin film on glass were investigated using the X-ray diffraction. The good crystalline structure is formed when substrate temperature is 150[.deg. C] and annealing condition is 550[.deg. C], 1[hour]. And the sensing properties at various thickness of the SnO$_{2}$ thin film and the effects of PdCI$_{2}$ addition were also investigated. The good result is showed when the thickness is below 1000[.angs.] and the quantity of PdCI$_{2}$ addition is 4[wt%]. The thickness of SnO$_{2}$ thin film was measured by .alpha.-step and Elliopsometer.