Pb(Mg1/3Nb2/3)O3 powder with high purity chemical homogeniety and reactivity was prepared by solvent eva-poration of common solution. The common solution was fabricated using a Pb(NO3)2 Mg(NO)3 and NB solution which was prepared by dissolving NbC in H2O2 acquous solution. In precusor powder prepared by solvent evaporation method the synthetic temperature of Pb(Mg1/3 Nb2/3)O3 phase was lowered. And the formation of homogeneous Pb(Mg1/3Nb2/3)O3 phase was enhanced but the formation of pyrochlore phase was reduced. The dielectric constant of PMN ceramics from the synthesized powder was found to increase with both sintering temperature and excess MgO and subsequent analysis of the microstructures confirmed that this was due to an increase in grain size. The grain size dependence is explained as a consequence of low-permittivity grain boundaries.