Polyimides containing cyclobutane ring in main chain is known to be thermally stable and able to be developed in organic solvents after photolysis with 254 nm UV light. This type of polyimides can be used as promising positive photoresist in VLSI fabrication process. In the current VLSI process, photoresist films are formed by spin coating. The film thickness is more than several hundred nano meters. It seems that there is room for improvement of film coating process by introducing Langmuir Blodgett technique. Thereby ultra thin film photoresist can be formed, and higher density of integration in VLSI be achieved. In the present work, depositing procedure of LB films of this polyimide was investigated. LB film thickness was measured by ellipsometry to evaluate deposited film status. Chemical imidization procedure was studied to avoid several problems in thermal imidization. The pattern of submicron dimension has successfully formed on LB film of 8nm thick, which found showing good contrast.