The quartemary system ceramics 0.5[xPb(Zn$_{1}$3/Nb$_{2}$3/)O$_{3}$-(1-x)Pb(Ni$_{1}$3/Nb$_{2}$3/)O$_{3}$]-0.5[yPbTiO$_{3}$-(1-y) PbZrO$_{3}$ for piezoelectric actuators were prepared bv the were added to the raw materials up to 5 mole. Sintering temperature was varied form 1000.deg. C to 1200.deg. C. Sintering characteristrics, dielectric and piezoelectric properties were then investigated. Piezoelectric properties of sample prepared by the molten salt method were improved compared to those prepared by the conventional method. Addition of PZN shifted morphotropic phase boundary to more Zr-rich composition and decreased the piezoelectric properties.