The corrosion fatigue test was conducted in air to investigate the corrosion fatigue strength of SM 30 C steel by which was corroded in the under sea and surface in the conditions of 3.0% NaCl salt solution. The fatigue tests were carried out on a rotary bending testing machine of cantilever type. The corrosion effect of the sea surface conditionwas served more than that of the under sea condition which was due ti the periodic contact of air thus accelerate the corrosion. The difference of the fatgue strength between sea surface and under sea conditions decreased with increase of stree level and corroded period. Inthe case of the solid shaft and thickness 2mm of hollow shaft, the difference of corrosion fatigue strength decreased as stress level and corrosion periodic increasing. Onthe contrary in the case of thickness 1mm of hollow sgaft, the difference of it increased as stress level, corrosionn periooodic increasing and also the condition of corrosion chaanged. The main factors affecting the degradation of fatigue strength due to corrosion were the reduction of sectional area and the increase of surface roughness. The interference phenomenon increase with stress level got higher.