A dry impregnation method was used for preparing pellet type Pt/$SnO_2$ gas sensor. The crystal structure, direction of the crystal, crystal size and microstructure between the catalyst and the support ($SnO_2$) were characterized with electron diffraction analysis, transmission electron microscopy, scanning electron microscopy. The characterization indicates that when Pt/$SnO_2$ sample is calcined at $400^{circ}C$, the Cl content associated with the Pt phase diminishes and the part of Pt is moved into $SnO_2$ support. This results in the enhancement of gas sensitivity. After the reactor with a Pt/$SnO_2$ sample was run with a flow rate of 30 sccm (a mixture of 0.5% $H_2$ in $_N2$) for a while, the resistance of $SnO_2$ was saturated, but the $SnO_2$ kept absorbing $H_2$ gas. This indicates that the surface state was saturated. For the 14 ppm $H_2$ gas, the sensitivity of Pt/$SnO_2$ devices was about 81% at an operating temperature of $300^{circ}C$.