It was succeeded in synthesizing the $Al_2O_3$-SiC refractory powders, which is main raw material of AlSiCa, from the domestic Hadong Kaolin. The oxidation reaction of the synthesized $Al_2O_3$-SiC powder was examined. The activation energy for SiC in $Al_2O_3$-SiC powder was calculated to be $Delta$G=74.86 KJ/mol in air, however the poor sinterability of the powders is thought to be due to the vaporization of SiC in $H_2$ atmosphere. The formation of the whisker-SiC gives the possibility in use for high temperature structural material over high temperature refractory brick.