Substrates, SiC raw materials and graphite crucibles were purified for growing the high quality 6H-SiC single crystal ingot. Especially, XRD data of raw materials were analyzed before and after purification. We have grown 6H-SiC single crystal ingot up to 33 mm in diameter and 11 mm in length and SiC wafer for using the substrate and observing the internal defects was about 33 mm in diameter and 0.5 mm in thickness. Utilizing optical microscpe and Raman spectroscopy, internal defects density and crystallinity of the SiC wafer obtained by purification processes before crystal growth were measured. As a result, micropipe density and planar defect density were 100/$ extrm{cm}^2$ and 30/$ extrm{cm}^2$ respectively. Therefore, high quality 6H-SiC single crystal could be grown because internal defects density of 6H-SiC single crystal ingot was decreased by the purification processes before crystal growth.