This paper reports on a thermodynamic analysis for the GaN thick film growth by vapor phase epitaxy method. The thermodynamic calculation was performed using a chemical stoichiometric algorism. The simulation variables include the growth temperature in a range 400~1500 K, the gas ratios $(GaCl_3)/(GaCl_3+NH_3)$ and $(N_2)/(GaCl_3+NH_3)$. The theoretical calculation predicts that the growth temperature of GaN be in the lower range of 450~750 K than the experimental results. The difference in the growth temperature between the simulation and the experiments indicates that the vapor phase epitaxy of GaN is kinetically limited, presumably, due to the high activation energy of thin film growth.