The physical properties of KLN single crystals very significantly according to the $Nb_2O_5$ content in grown crystal, therefore, it is very important to control the composition of KLN single crystals. In this study, KLN single crystals of high content $Nb_2O_5$ were grown by temperature fluctuation and TSSG (Top-seeded solution growth) methods with increasing the $Nb_2O_5$ content of starting solution. To investigate the existence of defect due to the increase of $Nb_2O_5$ content, dielectric and optical properties were measured. Due to the increase of defects in grown KLN single crystal, the shift of cutoff-frequency to lower energy and a broad Curie range, which shows the DPT (diffuse phase transition) characteristics, were observed.