The effect of softening point and glass amount of glass frit on the sintering behavior of low temperature cofirable glass/ceramic composites was studied and according to these results, glass/ceramic composites with high sintered density was fabricated. The density of composites was increased as the glass amount was increased. In case of using the glass with low softening point, the deformation of specimen was occurred though the ratio of the glass amount in the specimen was low. But, in case of using the glass with high softening point, the sintered density of composites was increased in accordance with glass amount. With the specimen of high softening point, the deformation was not happened. Therefore, it was found that the densification was progressed continuously in high glass amount. From the study on the effect of softening point of glass on sintering behavior, the suitable softening point and glass amount for fabrication of glass/ceramic composites can be anticipated. When glass frit with softening point of $790^{circ}C$ was chosen according to this result, low temperature cofirable glass/ceramic composites with high density (97%) at $900^{circ}C$ was fabricated.