For the fabrication of low temperature cofirable glass/ceramic with high dielectric constant, crystallizing glass [$SiO_2-TiO_2-RO (RO:BaO, CaO:SrO)$] was formed. The glass/ceramic composites were made by mixing this glass and alumina ceramic as filler, and its characteristics was investigated. With this glass compositon, it was possible to fabricate the glass which could be crystallized under $900^{circ}C$. And it was found that the crystallizing temperature was changed in accordance with the composition of RO in glass. By adding $Bi_2O_3$ as flux, using $Al_2O_3$ as filler and sintering at $860^{circ}C$, low temperature cofirable glass/ceramic with high dielectric constant was fabricated. The density of that composites was 3.96 g/$ extrm{cm}^3$, dielectric constant was 17 and Q. f was 600.