The effect of {{{{ {Ga }^{3+ } }} addition on the photoluminescence and cathodoluminescence of {{{{ {SrTiO}_{3 } }}:{{{{ { Pr}^{3+ } }} was stu-died by performing the excitation emission and decay time measurements. Addition of {{{{ {Ga }^{3+ } }} in {{{{ {SrTiO}_{3 } }}:{{{{ { Pr}^{3+ } }} resulted in a considerable enhancement of {{{{ { Pr}^{3+ } }} emission intensity. From the analysis of the experimental results the following mechanism is proposed. Excitation in the {{{{ {SrTiO}_{3 } }} host lattice leads to the formation of electrons in the conduction band and holes in the valence band. The electrons in the conduction band re-combine radiatively with the holes trapped at {{{{ { Ga}^{3+ } }} and the energy is transferred to {{{{ { Pr}^{3+ } }} ion which give its own characteristic red emission.