As results of the study on the sinterbility of YIG at the low temperature using CuO as additive CuO com-pound which contain {{{{ { {Fe }_{2 }O }_{3 } }} was shown liquid in sintering process. YIG crystal dissolved into CuO compound liquid phase and then Y element which is considered no solubility in solid CuO compound moved to the grain during cooling. The abnormal grain growth up to 150${mu}{ extrm}{m}$ at CuO 8.6mole% was shown due to shape accomdation reaction and local liquid distribution. The apparent density of YIG shows minimum at CuO 8.6 mole% due to abnormal grain growth and the saturation magnetization decrease dramatically at 32.5mole% due to orthoferrite formation.