The reaction-bonded TiC-Ni/Si/Co composites were prepared by the melt infiltration of Co, Si, and Ni me-tal into the TiC preforms. The miocrostructure reaction composition and mechanical properties were in-vestigated. In the case of the melt infiltrated with Co and Ni TiC grain shape was changed from angular to spherical shape with the average grain size of ∼5$mu extrm{m}$. In the case of the melt infiltrated with Co/Si or Ni/Si, Si was reacted with TiC particles and formed SiC particles. The bending strength of both specimens which have atomic ratio of 3 were 710 MPa and 515 MPa respectively. In the case of the melt infiltrated with Ni/Si/Co,. nonstoichiometric TiC was formed and its bending strength decreased to 420 MPa.