A carbon-containing silica glass was prepared from orgaincally modified silicate(Ormosil) by heat treatment in N2 atmosphere after the ormosil was synthesized using sol-gel method. The Ormosil was fabricated from the TEOS as the inorganic component and the PDMS as the organic component. The Ormosil changed to balck-coloured glass by carbon decomposed from the PDMS when the Ormosil was heated to 450$^{circ}C$ 20hrs. A dense silicon oxycarbide glass with 2.08 g/cm3 was obtained by heating the Ormosil at 1050$^{circ}C$ 10hrs. The microstructure of the carbon-containing silica glass was observed by SEM and the SiOxC4-x structure was confirmed by XPS measurement. The densification of the glass was studied by measurements of specific surface area linear shrinkage and geometric density.