In this study, the thermal property and adhesion of the electroless-deposited Cu thin film were investigated. The multilayered structure of Cu /TaN /Si was fabricated by electroless-depositing the Cu thin layer on the TaN diffusion barrier which was deposited by MOCVD on the Si substrate. The thermal stability was investigated by measuring the resistivity as post-annealing temperature for the multilayered Cu /TaN /Si specimen which was annealed at atmospheres of $H_2$and Ar gases, respectively. The adhesion strength of Cu films was evaluated by the scratch test. The adhesion of the electroless-deposited Cu film was compared with other deposition methods of thermal evaporation and sputtering. The scratch test showed that the adhesion of electroless plated Cu film on TaN was better than that of sputtered Cu film and evaporated Cu film.