Post-deposition vacuum annealing effects in electron-bearn-evaporated indium tin oxide (ITO) films have been investigated by the change of transmittance, sheet resistance and crystalline structure with annealing temperature ( $200-335^{circ}C$) and oxygen partial pressure ($1 imes^10^{-5}-1$ imes10^{-4} torr$) in air and vacuum. The sarnples were polycrystalline films with a preferred orientation in the (222) plan. High quality films with sheet resistance as low as 62 Q/O and transmittance over 99% (absentee layer at 500 nm) have been obtained by suitably controlling the vacuum annealing pararneters.neters.