In this study, mullite-zirconia comosite was fabricated by adding ZrOCl2.8H2O using of boehmite gel coating to Hadong kaolin (pink A grade) in order to enhance strength of the mullite specimens. The influence of ZrOCl2.8H2O content and fireing temperature on the crystall phase, microstructure, bulk density, strength of the specimens was investigated. Mullite-zirconia composite was produced in the process of coating zirconia to mullite powder synthesized thereafter and mixing simultaneously of starting materials with boehmite-zirconia gel. Maximum strength with in this study was 251 sintered at 1$600^{circ}C$ for 2h. Bulk density and strength of the composite with zirconia coated mullite was higher than simultaneous on mixture of starting materials.