Alumina tapes, having various ratios of alumina to alumina＋binder＋plasticizer (a/(a＋o)) and binder to binder＋plasticizer(b/(b＋p)), were prepared by the tape casting method. The tapes were thermocompressed varying the thermocompression parameters such as temperature, pressure, and duration time. Among the parameters, the pressure was the most influential to the tape packing density. The packing density varied in two different ways depending on the a/(a＋o) ratio. For the tapes having low a/(a＋o) ratio, a saturation density was reached by applying very a low pressure of 1 MPa. For tapes with high a/(a＋o), on the contrary, the saturation density was obtained at a relatively high pressure. These different responses to the pressure are attributed to the fact that the rearrangement of alumina particles by the pressure becomes easy as an organic content in the tapes is high.