KD₂PO₄ single crystals were grown from D₂O with reagent KH₂PO₄ and the crystal structure was determined by X-ray and neutron diffraction methods. The crystals are tetragonal at room temperature, I42d, with lattice parameters of a=7.4633(7), c=6.9785(5) Å and Z=4. Intensity data were collected on an Enraf-nonius CAD4 diffractometer with a graphite monochromated MoK_α radiation (λ=0.7107Å) and on the neutron four circle single crystal diffractometer with Ge(331) monochromated neutron beam (λ=0.997Å). The structure was refined by full-matrix least-square to final R and wR values of 0.030 and 0.072, respectively, for 204 observed reflections with I>2σ(I) by X-ray diffraction and to final R=0.041 and wR=0.096 for 144 observed relfecdtions by neutron diffraction. The O…O distance of 2.516(4)Å obtained by X-ray diffraction is the same as that of 2.515(4)Å by neutron diffraction. On the other hand, the O-D/H distance of 0.84(4)Å by X-ray diffraction is considerably shorter than 1.029(7) Åby neutron diffraction. Hydrogen and deuterium can be readily distinguished by neutrons. In this crystal 66% of H-positions were substituted by D and the rest 34% occupied by H. The phase transition temperature of DKDP obtained with deuteration levels is f193K. This value agrees fairly well with the result of DSC measurement. The nuclear density distribution by neutron diffraction provides an observation of the disordered state of D/H in KD₂PO₄ at room temperature.