$ZnGa_2O_4$ thin film phosphors have been deposited using a pulsed laser deposition technique on $Al_2O_3$(0001) substrates at a substrate temperature of $550^{circ}C$ with various oxygen pressures 100, 200 and 300 mTorr. The films grown under different growth oxygen pressures have been characterized using microstructural and luminescent measurements. The different photoluminescence (PL) characteristics with the increase in oxygen pressures may result from the change of the crystallinity and the composition ratio of Zn and Ga in the films. The luminescent spectra show a broad band extending from 300 to 600 nm peaking at 460 nm. The PL brightness data obtained from the $ZnGa_2O_4$ films grown under optimized conditions have indicated that the sapphire is a promising substrate for the growth of high quality $ZnGa_2O_4$ thin film phosphor.