Reverse-Water-Gas-Shift reaction (RWGSR) was carried out over the ZnO, $Al_2O_3,;and;ZnO/Al_2O_3$ catalysts at the temperature range from 400 to 700 ℃. The ZnO showed good specific reaction activity but this catalyst was deactivated. All the catalysts except the $ZnO/Al_2O_3$ catalyst (850 ℃) showed low stability for the RWGSR and was deactivated at the reaction temperature of 600 ℃. The $ZnO/Al_2O_3$ catalyst calcined at 850 ℃ was stable during 210 hrs under the reaction conditions of 600 ℃ and 150,000 GHSV, showing CO selectivity of 100% even at the pressure of 5 atm. The high stability of the $ZnO/Al_2O_3$ catalyst (850 ℃) was attributed to the prevention of ZnO reduction by the formation of $ZnAl_2O_4$ spinel structure. The spinel structure of $ZnAl_2O_4$ phase in the $ZnO/Al_2O_3$ catalyst calcined at 850 ℃ was confirmed by XRD and electron diffraction.