Ion implantation in polymeric materials can induce dramatic chemical modifications, such as bond breaking, cross linking, formation of new chemical products, which have strong influences on the macroscopic properties of the materials. In this study ion implantation was performed onto polymer, PC(polycarbonate), in order to investigate change of the optical transmittance property focusing ultraviolet ray range(200-400nm). PC was irradiated with N, Ar, Kr, Xe ions at the ion energy of 50keV and the dose range of 5 ${ imes}$ 10$^$15/, 1 ${ imes}$ 10$^$16/, 7${ imes}$10$^$16/ ions/$ extrm{cm}^2$. FT-IR, XPS, UV/Vis transmittance spectroscopy measurement technologies were employed to obtain chemical. structural properties and optical transmittance of irradiated polymer. The original PC(unimplanted) is quite transparent that it has more than 88% transmittance in the range UV-A(320∼400nm), but after ion implantation, surface colors were changed to the dark brown and the transmittance of UV ray decreased for all implantation condition, and the absorption edge was shift to visible range with increasing mass of implanted ion species and dose.