To make the all-solid-state lithium thin film battery having less than 1 fm in thickness, LiCoO$_2$ thin films were deposited on Pt/TiO$_2$/SiO$_2$/Si substrate as a function of Li/Co mole ratio and the deposition temperature by Pulsed Laser Deposition (PLD). Especially, LiCoO$_2$ thin films deposited at 50$0^{circ}C$ with target of Li/Co=1.2 mole ratio show an initial discharge capacity of 53 $mu$Ah/cm$^2$-$mu$m and capacity retention of 67.6％. The microstructural and electrochemical properies of (Li, La)TiO3 thin films grown on LiCoO$_2$Pt/TiO$_2$/SiO$_2$/Si structures by Pulsed Laser Deposition (PLD) were investigated at various deposition temperatures. The thin films grown at 10$0^{circ}C$ show an initial discharge capacity of approximately 51 $mu$Ah/cm$^2$-$mu$m and moreover show excellent discharge capacity retention of 90％ after 100 cycles. An amorphous (Li, La)TiO$_3$ solid electrolyte is possible for application to solid electrolyte for all-solid-state lithium thin film battery below 1 $mu$m.