The LTCCs (Low-Temperature Co-fired Ceramics) are very important for electronic industry to build smaller RF modules and to fulfill the necessity for miniaturization of devices in wireless communication industry. The dielectric materials with sintering temperature $T_{sint}$＜90$0^{circ}C$ are required. In this study, BaO-N $d_2$ $O_3$-Ti $O_2$ (BNT ： 20∼40 wt％) for ceramic materials and L $a_2$ $O_3$- $B_2$ $O_3$-Ti $O_2$ (LBT ： 80∼60 wt％) for crystallizable glasses were used. The glass/ceramic composites were investigated for sintering behavior, phase evaluation, densities, interface reaction and microwave dielectric properties. It was found that the addition LBT glass frist significantly lowered the sintering temperature to below 90$0^{circ}C$ and the densification with increasing addition LBT glass frist developed rapidly which was meant to be namely 90％ of relative density. The sintered bodies ekhibited applicable dielectric properties, namely 15 for $varepsilon$$_{r}$,, 10000 GHz for Q＊ $f_{0}$. The results suggest that the composites have good potential as a new candidate for LTCC materials.