The poly(1-trimethylsilyl-1-propyne) (PTMSP) and silica-filled PTMSP membranes were prepared by casting from a toluene solution on porous polyetherimide (PEI). FT-IR spectrum, GPC and SEM pictures have been taken to characterize the membranes. The particle size of membrane decreases as silica content of the membrane increases from 23 to 60 wt%, and a uniform distribution of the silica is observed. The separation properties of the gas mixture (32 mol% $H_2$/ 68 mol% $N_2$) through the composite membranes were studies as a function of pressure and percentage of silica. Selectivity values of $H_2$/$N_2$ increased as the pressure of permeation cell and silica content of the membrane increased. The real separation factor($alpha$), head separation factor($eta$), and tail separation factor((equation omitted)) of PTMSP-PEI composite membrane were 2.28, 1.58, and 1.44 respectively at $Delta$P 30 psi and $25^{circ}C$. $alpha$, $eta$, and (equation omitted) of PTMSP-Silica-PEI composite membrane for 60 wt% silica were 3.34, 1.95, 1.72 at $Delta$P 30 psi and $25^{circ}C$.