The porous SiO$_2$-B$_2$O$_3$ membrane was prepared from Si(OC$_2$$H_5$)$_4$-($CH_3$O)$_3$B-C$_2$$H_5$OH-$H_2O$ system by sol-gel method. In order to investigate the characteristics of this membrane, we examined that using BET, IR spectrophotometer, X-ray diffractometer, SEM and TEM. At $700^{circ}C$, the surface area of SiO$_2$-B$_2$O$_3$ membrane was 354.398 $m^2$/, the median pore diameter was 0.0048 ${mu}{ extrm}{m}$, and the particle size of SiO$_2$-B$_2$O$_3$ membrane was 7 nm. The separation properties of the gas mixture ($H_2$/$N_2$) through the SiO$_2$-B$_2$O$_3$ membrane was studied as a function of pressure. The real separation factor($alpha$) of SiO$_2$-B$_2$O$_3$ membrane for $H_2$/$N_2$ gas mixture was 4.68 at 155.15 cmHg and $25^{circ}C$. The real separation factor($alpha$), head separation factor($eta$) and tail separation factor((equation omitted)) were increased as the pressure of permeation cell increased.