IZO thin films are prepared on a corning 7059 glass substrate in a mixed gases of Ar +$O_2$ by rf-magnetron sputtering, using a powder target with a composition ratio of $In_{2}O_{3}$ : ZnO=90 : 10 $wt.\%$. Their electrical sheet resistance are strongly dependent on the oxygen concentration introduced during the deposition, a minimum resistivity of $3.7 imes10^{-4}Omegacdot$ cm and an average transmittance over $85\%$ in the visible range are obtained in a film deposited in pure Ar gas which is close to near the stoichiometry. During the heat treatment from room temperature up tp $600^{circ}C$ in various environments, the electrical resistance changes are explained by cyrstallizations or oxidizations of In metal and InO contained in the IZO film. The electrical properties due to oxygen adsorption and phase transitions occurring at temperatures over $40000^{circ}C$ during heat treatment in air are also investigated.