In this study, the high strength and superior toughness spring steels as the suspension material, used for automobile and railroad industries were utilized to carry out the following investigations. Corrosion times were controlled in 7, 14,30 and 60days to examine the relation between corrosion pit and compressive residual stress in the static corrosion environment after shot peened. And then corrosion current and corrosion potential were measured for every 24 hours to investigate the corrosion mechanism. Shot peened material shows the low or rate of corrosion current as compared with unpeened material. In case of hot peened material which has the highest residual stress, it has a low corrosion current density.