In this study, divalent europium-activated $NaCaPO_4$ green phosphor powders were prepared by the chemical synthetic method followed by heat treatment in reduced atmosphere, and the crystal structures, morphologies and photoluminescent properties of the powders were investigated by x-ray powder diffraction, scanning electron microscope and spectrometer for the first time. The effects of Ca/P and Na/Ca mole ratios on the final products were also investigated. The influences of input amount change of europium as the activator on the light emission intensity were studied, and the resulting concentration quenching phenomenon was observed. The optimized synthesis conditions obtained in this study were Ca/P mole ratio 1.2, Na/Ca mole ratio 3.0 and 4 mole%Eu. The peak wavelength was 505 nm for all the samples. The result of excitation spectrum measurement indicated that the excitation efficiency was high for the long-wavelength UV region. It was thus concluded that the samples prepared in this study can be successfully applied for the light-emitting devices such as LED excited with long-wavelength UV light sources.