The surface modification of automobile parts is of great technological importance for the improvement of corrosion resistance, wear resistance, fatigue strength and so on. Recently, research on the development of the technology of surface modification substituting 6-balance chrome process has progressively been achieved in automobile parts. Although the innovation technology for the improvement of the corrosion-resisting and wear resistant properties through post oxidation after nitrocarburising process had attracted a great attention. For this, anodically potentiodynamic polarisation testing was carried out to corrosion resistance and friction and wear experiment according to applied load and sliding distance was carried out to evaluate the wear resistance of machine structural steel with nitrocarburising and non-nitrocarburising SM45C. The presumed wear volume was calculated with the image processing far evaluation of wear resistance of two materials. The results show that the nitrocarburising had a distinguished corrosion resistance and wear resistance than non-nitrocarburising.