In the load-carrying fillet weldments, which are common in ship structures, fatigue cracks can occur at the weld root, in addition to the weld toe. In particular, fatigue cracks originating from the weld root are difficult to detect and cause a significant reduction in the fatigue strength of a weldment. Therefore, it is important to note the fatigue failure mode of load-carrying fillet weldment. In this study, a series of fatigue test was carried out for the fatigue strength evaluation of longi-web connections that are typical kinds of the load-carrying fillet weldment.